Test Reports

S. No. Mineral Material Code Use(s) Report(s)
1. Raw Kaolin Lumps (Crude China Clay) White Clay
  1. Double Charge Tiles
  2. Slabs
  3. Full Body Tiles
  4. Glaze Compound
 PDF
L White Clay
  1. Sanitaryware
  2. Tableware
  3. Glaze Compound
 PDF
SM-1
  1. Nano Tiles (Single Charge)
  2. GVT Tiles
  3. Parking Tiles
  4. Porcelain Tiles
  5. Full Body Tiles
  6. Double Charge (Lower Body)
 PDF

RD-2
  1. Nano Tiles (Single Charge)
  2. GVT Tiles
  3. Parking Tiles
  4. Porcelain Tiles
  5. Full Body Tiles
  6. Double Charge (Lower Body)

PDF

WN-1
  1. Nano Tiles (Single Charge)
  2. GVT Tiles
  3. Parking Tiles
  4. Porcelain Tiles
  5. Full Body Tiles
  6. Double Charge (Lower Body)

PDF

JSN-2
  1. Nano Tiles (Single Charge)
  2. GVT Tiles
  3. Parking Tiles
  4. Porcelain Tiles
  5. Full Body Tiles

PDF

JN-2
  1. Nano Tiles (Single Charge)
  2. GVT Tiles
  3. Parking Tiles
  4. Porcelain Tiles
  5. Full Body Tiles
  6. Double Charge (Lower Body)

PDF

2.

Washed Kaolin Lumps (Levigated China Clay)

D SUPER
  1. Tiles
  2. Sanitaryware
  3. Tableware
  4. Glaze Compound

PDF

D WHITE

3.

Kaolin Noodle

SB-NO
  1. Glaze Compound
  2. Ceramic Engobe
  3. Sanitaryware
  4. Tableware
  5. Tiles

PDF

4.

Calcined Kaolin Powder (500-700 mesh)

SB-DM
  1. Paints
  2. Paper

PDF

SB-SNOW

SB-SUPER

5.

Hydrous Kaolin Powder (300-700 mesh)

SB-87
  1. Paints
  2. Paper
  3. Rubber
  4. Fiberglass

PDF

SB-85

SB-83

SB-80

6.

Ball Clay Lumps

MK-1
  1. Insulator
  2. Sanitaryware
  3. Stoneware

PDF

DN-1

  1. Nano Tiles (Single Charge)
  2. GVT Tiles
  3. Parking Tiles
  4. Porcelain Tiles
  5. Full Body Tiles
  6. Double Charge (Lower Body)

PDF

N-2

  1. Nano Tiles (Single Charge)
  2. GVT Tiles
  3. Parking Tiles
  4. Porcelain Tiles
  5. Full Body Tiles
  6. Double Charge (Lower Body)

PDF

TN-1
  1. Nano Tiles (Single Charge)
  2. GVT Tiles
  3. Parking Tiles
  4. Porcelain Tiles
  5. Full Body Tiles
  6. Double Charge (Lower Body)

PDF

SN-1
  1. GVT Tiles

PDF

MSU (High Silicious Clay)
  1. Cement

PDF

BS-3 (High Silicious Clay)
  1. Cement

PDF

7.

Ball Clay Powder (300-500 mesh)

SB-KH
  1. Kraft Paper
  2. Rubber
  3. Pesticides
  4. Soaps & Detergents

PDF

8.

Potassium Feldspar Lumps & Chips

SB-PFL
  1. Tiles
  2. Sanitaryware
  3. Tableware
  4. Glass
  5. Glaze

Enquire

9.

Potash Feldspar Powder

SB-PF

Enquire

10.

Sodium Feldspar Lumps & Chips

SB-SFL

Enquire

11.

Sodium Feldspar Powder

SB-SF

Enquire

12.

Quartz Lumps

SB-QL
  1. Tiles
  2. Sanitaryware
  3. Tableware
  4. Glass
  5. Frits

PDF

13.

Quartz Powder

SB-QP

Enquire

14.

Silica Sand

SB-SS
  1. Glass
  2. Foundry
  3. Construction
  4. Ceramics
  5. Refractory

PDF

Kaolin Technical Data Sheet

PHYSICAL PROPERTIES
CS 1 JN 2 JSN 2 L White Clay White Clay RD 2 SM 1 WN 1
Shrinkage % 5.94 8.47 11.17 5.96 12.12 10.74 11.14 10.14
Loss On Ignition % 10.02 12.82 11.82 12.52 12.91 9.91 11.58 11.58
Dry M.O.R Kg cm2 23.7 29.2 28.4 24.3 25.4 22.7 30.8 26.8
Fired M.O.R Kg cm2 257.9 303.4 341.6 225.9 212.8 283.2 317.4 267.4
Water Absorption % 8.83 2.64 3.65 13.75 5.33 6.26 6.52 6.52
Water Of Plasticity % 31.2 38.4 36.2 34.8 35.2 32.6 36.4 36.4
T.D.S 220 480 500 530 230 400 320 320
Residue % 1.24 1.72 0.28 0.82 0.18 0.26 0.52 0.52
L * 88.35 81.11 75.61 91.32 92.33 73.36 86.72 84.72
A * 1.19 2.12 2.15 0.73 0.36 5.56 1.5 1.5
B * 11.96 13.72 12.13 10.7 8.46 13.36 14.46 14.46
Whiteness (after firing) 72.6 58.04 49.94 78.65 79.19 54.23 71.11 71.11
Whiteness (before firing) 84.9 81.9
Temperature 1195/1207 1188/1196 1188/1196 1186/1196 1205/1220 1188/1205 1188/1196 1188/1196
Cycle Min.45 45 55 55 48 60 45 55 55
CHEMICAL PROPERTIES
SiO2 % 55.89 49.58 48.2 48.51 46.02 54.52 50.56 49.56
AI2O3 % 27.91 30.72 33.52 32.14 36.34 29.85 35.46 33.46
Fe2O3 % 1.04 1.09 1.75 0.92 0.62 1.56 1.51 1.21
TiO2 % 1.17 1.22 1.36 1.17 1.01 1.35 1.01 1.52
CaO % 0.89 0.86 0.82 0.54 0.32 0.39 0.64 0.34
MgO % 0.4 0.68 0.64 0.56 0.28 0.21 0.57 0.47
K2O % 1.06 0.89 1.03 1.08 0.54 1.45 0.82 1.12
Na2O % 0.46 0.36 0.38 0.83 0.56 0.26 0.32 0.32
Loss on Ignition % 9.95 13.04 11.69 12.81 13.61 10.01 11.68 11.68

Ball Clay Technical Data Sheet

PHYSICAL PROPERTIES
DN 1 MK 1 N 2 MSU TN 1 BS 3
Shrinkage % 12.29 7.9 10.13 3.09 9.92 8.51
Loss On Ignition % 9.74 11.79 10.67 6.56 9.81 8.27
Dry M.O.R Kg cm2 35.9 28.9 33.1 20.9 30.4 24.7
Fired M.O.R Kg cm2 338.3 254.1 354.6 211.8 335 303.1
Water Absorption % 4.34 3.55 4.61 12.26 2.88 6.46
Water Of Plasticity % 40 34.6 38.4 27.6 38.2 31.8
T.D.S 450 594 1120 1140 1030 830
Residue % 0.66 0.38 1.48 2.63 0.34 0.51
L * 84.52 84.74 85.38 86.44 78.33 72.63
A * 2.31 1.24 2.4 2.2 2.4 4.87
B * 12.42 16.45 11.06 12.53 13.9 22.52
Whiteness (after firing) 55.67 54.12 60.54 68.81 43.22 44.78
Temperature 1198/1205 1210/1215 1181/1188 1186/1201 1188/1196 1181/1192
Cycle Min. 55 62 55 45 55 51
CHEMICAL PROPERTIES
SiO2 % 46.25 50.01 54.72 69.06 54.73 60.85
AI2O3 % 34.76 32.78 29.58 19.58 28.32 24.05
Fe2O3 % 1.68 0.87 0.87 0.87 1.14 1.82
TiO2 % 0.75 1.04 1.52 2.14 1.27 3.09
CaO % 0.51 0.31 0.71 0.29 0.98 0.48
MgO % 0.81 0.65 0.38 0.24 0.71 0.51
K2O % 0.91 1.14 0.53 0.63 1.69 1.05
Na2O % 0.35 0.65 0.59 0.29 0.37 0.47
Loss on Ignition % 13.15 11.65 10.84 6.53 10.08 8.45